XCEL IGA is an instant grab MS Polymer adhesive. It was developed for high strength initial bond. It fixes large panels and heavy objects without support or mechanical fixings, and has high tensile strength. It cures without shrinking, resists vibrations and remains flexible. It is available in 2 colours, grey and white.
| Raw material basis: | MS Polymer |
| Consistency: | Non-slump paste |
| Specific gravity: | approx. 1.30 +/- 0.02 |
| Skin forming time: | Less than 20 minutes (at 23ºC; 50% R.H.) |
| Curing rate: | 2-3 mm/24 hr |
| UV Resistance (ASTM G26): | After 2000 hours UV-A no change in appearance or physical properties |
| Consumption: | approx. 50 ml/ linear meter (nozzle diameter: 8mm) |
| Application temperature: | Between 5ºC to 40 ºC |
| Properties of the cured product: | (After one week at 23ºC and 50% R.H.) |
| Service temperature: | -40ºC to +100ºC (short exposure at 140ºC) |
| 100% Modulus (ASTM D412 *Rate = 2”/minute) : | 118Psi |
| Shore A hardness (ISO 868): | 57 +/- 5 |
| Max. tensile strength (ASTM D412 *Rate = 2”/minute): | 40kg / cm2 / 575 Psi |
| Peel Strength (ASTM C794) | 110 Pli |
| Elongation: | > 110 % |
| Movement Capability: | 25% |